The phase diagram of the Fe-P binary system at 3 GPa and implications for phosphorus in the lunar core
Yuan Yin;  Zeming Li;  Shuangmeng Zhai
2019
发表期刊Geochimica et Cosmochimica Act
卷号254页码:54-66
摘要

Phosphorus is a potential candidate in the metallic core of the Moon. The phase diagram of the Fe-P binary system was investigated at the pressure of 3 GPa and temperatures of up to 1600 °C. Up to 3.0 wt% and 10.4 wt% phosphorus can dissolve in the solid iron and liquid Fe-P phases at 1100 °C and 3 GPa, respectively. The eutectic temperature on the iron-rich side was determined as 1085 °C at 3 GPa. The solubility of phosphorus in the iron decreases from ∼1.4 wt% at 1100 °C to ∼0.7 wt% at 1500 °C and 3 GPa. Structure of the solid iron in the quenched sample is the body-center cubic, corresponding to α-Fe phase. Extending the phosphorus solubility in the solid iron to the present lunar core conditions yields a maximum phosphorus concentration in a fully crystallized iron core of 0.85 ± 0.15 wt%. If there are Ni and C in the core, the value would be depressed to 0.4 ± 0.1 wt%. In addition, based on a simple siderophile mass balance between the bulk Moon (BM) and bulk silicate Moon (BSM) and a modeled phosphorus partition coefficient, DP-Mooncore/mantle (40–200) for the lunar magma ocean, a bulk silicate Earth-like P content (82 ± 8 ppm) in the initial Moon yields a lunar core with <0.3 wt% P. Some other potential light elements such as S and C could reduce the P content in the lunar core. Furthermore, the partition coefficient of phosphorus in the iron and liquid melt (DPSM/LM) was found to be 0.10 ± 0.03 at 3 GPa. Taking the sulfur into account, the DPSM/LM increase to 0.18 ± 0.02 at 5 GPa in the S-rich liquid metal (∼8 wt%). In the case of a solid lunar inner core and S-bearing liquid outer core, their P contents were assessed to be less than 0.09 ± 0.01 wt% and 0.51 ± 0.01 wt%, respectively, when the lunar core’s storage of P is <0.3 wt%. The moderate phosphorus solubility in the solid iron, combined with the assumption of abundant phosphorus in the bulk Moon, indicates that the phosphorus concentration in the lunar core could higher than previously thought.

关键词Fe-p Binary System high Pressure phase Diagram lunar Core
收录类别SCI
语种英语
文献类型期刊论文
条目标识符http://ir.gyig.ac.cn/handle/42920512-1/10872
专题地球内部物质高温高压实验室
作者单位1.Key Laboratory of High-temperature and High-pressure Study of the Earth’s Interior, Institute of Geochemistry, Chinese Academy of Sciences, Guiyang 550081, China
2.University of Chinese Academy of Sciences, Beijing 100049, China
推荐引用方式
GB/T 7714
Yuan Yin;Zeming Li;Shuangmeng Zhai. The phase diagram of the Fe-P binary system at 3 GPa and implications for phosphorus in the lunar core[J]. Geochimica et Cosmochimica Act,2019,254:54-66.
APA Yuan Yin;Zeming Li;Shuangmeng Zhai.(2019).The phase diagram of the Fe-P binary system at 3 GPa and implications for phosphorus in the lunar core.Geochimica et Cosmochimica Act,254,54-66.
MLA Yuan Yin;Zeming Li;Shuangmeng Zhai."The phase diagram of the Fe-P binary system at 3 GPa and implications for phosphorus in the lunar core".Geochimica et Cosmochimica Act 254(2019):54-66.
条目包含的文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
The phase diagram of(3391KB)期刊论文作者接受稿开放获取CC BY-NC-SA浏览 请求全文
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Yuan Yin;Zeming Li;Shuangmeng Zhai]的文章
百度学术
百度学术中相似的文章
[Yuan Yin;Zeming Li;Shuangmeng Zhai]的文章
必应学术
必应学术中相似的文章
[Yuan Yin;Zeming Li;Shuangmeng Zhai]的文章
相关权益政策
暂无数据
收藏/分享
文件名: The phase diagram of the Fe-P binary system at 3 GPa_and implications for phosphorus in the lunar core.pdf
格式: Adobe PDF
此文件暂不支持浏览
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。