Preparation of a La/N co-doped TiO2 film electrode with visible light response and its photoelectrocatalytic activity on a Ni substrate | |
Xiao Zhou; Xiaona Zhang; Xinbin Feng; Juan Zhou; Shaoqi Zhou | |
2016 | |
发表期刊 | Dyes and Pigments |
卷号 | 125页码:375-383 |
摘要 | To prevent the recombination of photoelectron hole pairs and to extend the adsorption in the visiblelight region, a TiO2 coating co-doped with lanthanum and nitrogen on nickel foam was successfully prepared through sol gel and dip coating methods using the precursors butyl titanate (TBOT) for Ti, lanthanum trioxide for La and urea for nitrogen. The photoelectrocatalytic properties of the prepared samples in the degradation of malachite green were examined under visible light. The phase composition, crystalline structure and optical properties of the La/N co-doped TiO2(Ni) photo-electrodes were studied using different measurement methods, including XRD, SEM, UV-vis DRS, Raman and FUR. The results indicated that the co-doped TiO2(Ni) photo-electrode not only effectively restrained the growth of the TiO2 grains, but also inhibited the transformation of the titania phase from anatase to rutile. The photo-response of the modified samples was substantially extended from 400 nm to 480 nm, and the band gap narrowed from 3.2 eV to 2.79 eV. The co-doped TiO2(Ni) samples exhibited higher photocatalytic activity as a result of the synergistic effects of the La and N co-doping. The degradation rate of malachite green by the La0.2%N20%/TiO2(Ni) photo-electrode was 23.5% higher than that of the un-doped sample; this result indicated that the extended range of responsive wavelengths greatly expanded the possible applications of the modified electrode. When a low bias voltage was applied to the La0.2%N20%/ TiO2(Ni) photo-electrodes, the electrodes exhibited even better photoelectrochemical properties and photoelectrocatalytic activity than a La0.2%N20%/TiO2(Ni) film under visible light irradiation. |
关键词 | La/n Co-doping Tio2 Ni Foam Substrate Photoelectrocatalysis Visible Light Mechanistic Considerations |
收录类别 | SCI |
语种 | 英语 |
文献类型 | 期刊论文 |
条目标识符 | http://ir.gyig.ac.cn/handle/42920512-1/8204 |
专题 | 环境地球化学国家重点实验室 |
作者单位 | 1.Institute of Biology, Guizhou Academy of Sciences, Shanxi Road 1, Guiyang, 550001, PR China 2.College of Environment and Energy, South China University of Technology, Guangzhou Higher Education Mega Center, 510006, PR China 3.State Key Laboratory of Subtropical Building Sciences, South China University of Technology, Guangzhou, 510641, PR China 4.College of Chemical Biology and Material Science, East China Institute of Technology, Guanglan Road No. 418, Nanchang, 330013, PR China 5.Institute of Geochemistry, Chinese Academy of Sciences, Naming Road No. 46, Guiyang, 550001, PR China |
推荐引用方式 GB/T 7714 | Xiao Zhou,Xiaona Zhang,Xinbin Feng,et al. Preparation of a La/N co-doped TiO2 film electrode with visible light response and its photoelectrocatalytic activity on a Ni substrate[J]. Dyes and Pigments,2016,125:375-383. |
APA | Xiao Zhou,Xiaona Zhang,Xinbin Feng,Juan Zhou,&Shaoqi Zhou.(2016).Preparation of a La/N co-doped TiO2 film electrode with visible light response and its photoelectrocatalytic activity on a Ni substrate.Dyes and Pigments,125,375-383. |
MLA | Xiao Zhou,et al."Preparation of a La/N co-doped TiO2 film electrode with visible light response and its photoelectrocatalytic activity on a Ni substrate".Dyes and Pigments 125(2016):375-383. |
条目包含的文件 | ||||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
Preparation of a La_(1422KB) | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | 浏览 请求全文 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论